Use este identificador para citar ou linkar para este item: http://www.repositorio.cdtn.br:8080/jspui/handle/123456789/1286
Título: Enamel loss and superficial aspect during bonding and bedonding of metallic brackets
Título do periódico: Bioscience Journal
Autor(es): Ferreira, Emanuelle de Fátima
Vilani, Giselle Naback Lemes
Jansen, Wellington Corrêa
Brito, Hélio Henrique de Araújo
Neto Ferreira, Ricardo Alberto
Manzi, Flávio Ricardo
Oliveira, Dauro Douglas
Afiliação: Pontificia Universidade Catolica de Minas Gerais, PUCMINAS, Belo Horizonte, MG, Brasil
Pontificia Universidade Catolica de Minas Gerais, PUCMINAS, Belo Horizonte, MG, Brasil
Pontificia Universidade Catolica de Minas Gerais, PUCMINAS, Belo Horizonte, MG, Brasil
Centro de Desenvolvimento da Tecnologia Nuclear, CDTN, Belo Horizonte, MG, Brasil
Pontificia Universidade Catolica de Minas Gerais, PUCMINAS, Belo Horizonte, MG, Brasil
Pontificia Universidade Catolica de Minas Gerais, PUCMINAS, Belo Horizonte, MG, Brasil
Data do documento: 2016
Palavras-chave: Brackets
Resumo: To evaluate the cumulative enamel loss during bonding and debonding procedures of orthodontic metallic brackets and to analyze the enamel superficial roughness. Forty-seven maxillary first premolars were obtained for quantitative and qualitative analysis. For quantitative analysis, forty premolars were weighed at each stage of treatment and the equivalent thickness of enamel loss was measured. The amount of tooth mass loss in each stage was divided by the density value to obtain the corresponding enamel volume lost. Subsequently, these volumes were divided by a circular area with a diameter of 7 mm, thus obtaining the equivalent thickness of enamel loss. They were assessed under the following conditions: as sound enamel, after acid conditioning, following the removal of residual resin composite, after final polishing with high or low-speed, and with or without water refrigeration. A rugosimeter was used to obtain a graphic registration of the enamel superficial roughness before and after acid conditioning. The data were analyzed with the Quantikov software and the Shapiro Wilk’s and Wilcoxon statistical tests were used to evaluate enamel superficial roughness. The one-way ANOVA followed by Bonferroni Post-Hoc tests were used to analyze the amount of enamel loss. For qualitative analysis, scanning electron microscopy (SEM) of the enamel surfaces was performed on seven premolars, one in each step. Acid conditioning significantly increased enamel surface roughness (p<0.01). Based on the dental mass weighed after each stage of evaluation, enamel loss was statistically significant in all stages (p<0.01). However, when the 4 different final polishing methods were compared, no statistically significant differences were registered regarding loss of mineralized structure (p=0.72). The SEM analysis revealed that the tungsten-carbide bur with water refrigeration and lowspeed rubber points caused less damage to the enamel. The greatest amount of enamel loss was due to acid conditioning. The losses relative to abrasion with composite removal or after the 4 polishing protocols were similar. Finally, none of the enamel surfaces was restored to their original aspects after bonding and debonding metallic brackets.
Acesso: L
Aparece nas coleções:Artigo de periódico

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Enamel loss and superficial aspect during bonding.pdf562.49 kBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.